BambuLab PAHT-CF Black (70100) com bobina, 0,5 kg

BambuLab PAHT-CF is a high-performance polyamide (nylon) filament reinforced with 15% carbon fiber, designed for demanding industrial applications. This black filament offers exceptional strength, stiffness, and heat resistance, making it ideal for functional prototypes, jigs, fixtures, and end-use parts. The 0.5kg spool is perfect for smaller projects or testing.

Advantages

High tensile strength (70 ± 5 MPa) and flexural modulus (4000 ± 200 MPa) ensure durable, rigid prints. With a heat deflection temperature of 150°C (0.45 MPa), parts maintain integrity under high temperatures. The carbon fiber reinforcement reduces warping and improves dimensional stability.

Suitable for

• Functional prototypes
• Jigs and fixtures
• Industrial components
• Automotive and aerospace parts
• High-temperature applications

Key specifications

• Material: PAHT-CF (Polyamide High-Temperature Carbon Fiber)
• Color: Black
• Filament diameter: 1.75 mm
• Net weight: 0.5 kg
• Printing temperature: 280-300 °C
• Bed temperature: 90-110 °C (with glue stick)
• Recommended nozzle: Hardened steel, ≥ 0.4 mm
• Density: 1.25 g/cm³
• Carbon fiber content: 15%
• Spool type: Plastic spool
• AMS compatibility: Not recommended

Recommendations

For best results, dry the filament before use (moisture sensitive). Use a hardened steel nozzle due to abrasive carbon fiber. Ensure proper bed adhesion with a glue stick. Not recommended for AMS due to stiffness.